Ultramid? 1503-2 NF2004 | PA66-GF33 | BASF

 二维码 2
Ultramid? 1503-2 NF2004 | PA66-GF33 | BASF
材料文字说明
Ultramid? 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
机械性能干 / 已调节单位测试标准
拉伸模量10800 / 7400MPaISO 527-1/-2
断裂应力210 / 145MPaISO 527-1/-2
断裂伸长率3 / 5%ISO 527-1/-2
无缺口简支梁冲击强度, +23°C90 / 100kJ/m2ISO 179/1eU
无缺口简支梁冲击强度, -30°C75 / 75kJ/m2ISO 179/1eU
简支梁缺口冲击强度, +23°C12 / 15kJ/m2ISO 179/1eA
简支梁缺口冲击强度, -30°C11 / 11kJ/m2ISO 179/1eA
热性能干 / 已调节单位测试标准
熔融温度, 10°C/min257 / *°CISO 11357-1/-3
热变形温度, 1.80 MPa255 / *°CISO 75-1/-2
热变形温度, 0.45 MPa264 / *°CISO 75-1/-2
其它性能干 / 已调节单位测试标准
吸水性5.7 / *%类似ISO 62
吸湿性1.7 / *%类似ISO 62
密度1400 / -kg/m3ISO 1183
函数
www.campusplastics.com02468050100150200250应力-应变.Ultramid? 1503-2 NF2004 (干)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com01234567050100150应力-应变.Ultramid? 1503-2 NF2004 (湿)应变 in %应力 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com02468020004000600080001000012000正割模量-应变.Ultramid? 1503-2 NF2004 (干)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
www.campusplastics.com0123456710002000300040005000600070008000正割模量-应变.Ultramid? 1503-2 NF2004 (湿)应变 in %正割模量 in MPa23°C40°C80°C120°C150°CB折断BBBBB
典型数据
加工方法
注塑


会员登录
登录
我的资料
我的收藏
留言
回到顶部
http://www.bare77.com http://www.stingyjackspumpkinpatch.com http://www.ah-hsw.com http://www.stingyjackspumpkinpatch.com http://www.karlonlife.com http://www.wtfffff.com http://www.anastasialux-photography.com http://www.hzyongan.com http://www.fcbchina.com http://www.hlhgzj.com http://www.9539000.com http://www.tallerecommerce.com http://www.mba-plus.com http://www.zghydk.com http://www.xt-founder.com http://www.radeap.com http://www.gift16888.com http://www.jumpstartcreditservices.com http://www.lzjklxx.com http://www.carpetcleaningeasthills.com http://www.jovensinc.com http://www.rootlesssalon.com http://www.xjtsxb.com http://www.brunswickbulldogsnyfl.com http://www.loststocktonstories.com http://www.syshenger.com http://www.sqllx.com http://www.hechengdong.com http://www.liumeiquan.com http://www.lawyer006.com